Influence of rising rate of power during laser sintering Ba 0.5Sr1.5Na0.6K0.4Nb 5O15 ceramics - 文章详情页

作者：

Du, Xinyu (Du, Xinyu.) | Ji, Lingfei (Ji, Lingfei.) (学者：季凌飞) | Jiang, Yijian (Jiang, Yijian.) (学者：蒋毅坚)

收录：

EI Scopus

摘要：

Tungsten　bronze　Ba0.5Sr1.5Na0.6K　0.4Nb5O15ceramics　with　97%　theroetical　density　have　been　prepared　successfully　by　CO2　laser　sintering.　The　laser　power　rising　rate　of　1　W/s　is　the　best　technical　parameter　for　obtaining　dense　ceramics.　The　temperature　field　analysis　reveals　that　the　lower　rising　rate　of　power　can　avoid　the　appearance　of　hollow　structure　in　the　sample.　©　2009　IEEE.

关键词：

Barium compounds Bronze Carbon dioxide lasers Laser heating Niobium compounds Potassium compounds Sintering Sodium compounds Strontium compounds

作者机构：

[ 1 ] [Du, Xinyu]Institute of Laser Engineering, Beijing University of Technology, Beijing 100124, China
[ 2 ] [Ji, Lingfei]Institute of Laser Engineering, Beijing University of Technology, Beijing 100124, China
[ 3 ] [Jiang, Yijian]Institute of Laser Engineering, Beijing University of Technology, Beijing 100124, China

通讯作者信息：

电子邮件地址：

glacier@emails.bjut.edu.cn

查看成果更多字段

成果类型
所属机构

所有年份指定年份从至