Rapid CO2 laser sintering of Ba0.5Sr 1.5Na0.6K0.4Nb5O15 piezoelectric ceramic - 文章详情页

作者：

Du, Xinyu (Du, Xinyu.) | Ji, Lingfei (Ji, Lingfei.) (学者：季凌飞) | Jiang, Yijian (Jiang, Yijian.) (学者：蒋毅坚)

收录：

EI Scopus

摘要：

Dense　tungsten　bronze　Ba0.5Sr1.5Na　0.6K0.4Nb5O15　[(BSKNN)　x=1.5,　y=0.4]　piezoelectric　ceramic　is　produced　by　CO2　laser　sintering　method　of　9　minute　duration.　The　observed　XRD　spectra　indicate　that　both　laser　sintered　and　furnace　sintered　ceramic　are　of　crystallized　tungsten　bronze　structure.　Microstructure　examination　of　both　laser　and　furnace　sintered　ceramics　show　the　former　have　smaller　grain　size,　fewer　pores　and　a　greater　density　of　4.87　g/cm3.　The　laser　sintered　Ba0.5Sr1.5Na　0.6K0.4Nb5O15　[(BSKNN)　x=1.5,　y=0.4]　ceramic　demonstrate　piezoelectric　properties　for;　maximum　reached　polarization　and　remnant　polarization,　Pm=8.27　μC/cm2　and　P　r=3.25　μC/cm2,　coercive　field　of　Ec=7.01　kV/cm.　The　piezoelectric　constant　d33=55　pC/N.

关键词：

Barium compounds Bronze Carbon dioxide Carbon dioxide lasers Ceramic materials Laser heating Niobium compounds Piezoelectric ceramics Piezoelectricity Polarization Sintering Sodium compounds Strontium compounds Tungsten

作者机构：

[ 1 ] [Du, Xinyu]Institute of Laser Engineering, Beijing University of Technology, Beijing, 100124, China
[ 2 ] [Ji, Lingfei]Institute of Laser Engineering, Beijing University of Technology, Beijing, 100124, China
[ 3 ] [Jiang, Yijian]Institute of Laser Engineering, Beijing University of Technology, Beijing, 100124, China

通讯作者信息：

电子邮件地址：

查看成果更多字段

成果类型
所属机构

所有年份指定年份从至