Texture　evolution　and　plastic　deformation　mechanism　of　the　weld　zones　of　magnetic　pulse　welded　dissimilar　1060　pure　Al　and　AZ31B　Mg　alloy　have　been　investigated　in　the　present　work.　A　much　refined　microstructure　with　smaller　grains　and　higher　hardness　was　observed　near　the　weld　interface　which　has　different　texture　types　compared　to　the　BM　(base　material)　at　both　the　Al　side　and　the　Mg　side.　The　intermetallic　layers　at　the　interface　of　the　Al　side　and　the　Mg　side　have　the　highest　hardness.　The　region　near　the　weld　interface　has　higher　activity　of　both　slip　and　twinning.　Slip　occurs　on　two　planes　(111)　and　((1)　over　bar　11)　in　the　Al　BM,　while　the　active　slip　systems　in　the　Al　region　near　the　weld　interface　are　on　four　planes　(111),　(11　(1)　over　bar),　((1)　over　bar　11)　and　(1　(1)　over　bar　1).　The　transition　of　single　texture　in　the　BMto　complex　texture　type　in　the　region　near　the　weld　interface　at　both　the　Al　side　and　the　Mg　side　was　due　to　{111}　slip　and　{10　(1)　over　bar2}　twinning,　respectively.