In　this　paper,　MOF-derived　N-doped　porous　carbon　anchoring　Sn4P3　(Sn4P3@NPC)　composite　is　prepared　via　a　low-temperature　phosphidation　reaction　with　SnO2@NPC　composite　as　the　precursor.　The　as-prepared　Sn4P3@NPC　composite　exhibit　a　high　stable　capacity　of　319　mAh　g(-1)　at　0.1　A　g(-1)　after　100　cycles　and　improved　rate　performance　(the　capacities　of　365,　322,　260,　204,　and　146　mAh　g(-1)　at　0.1,　0.2,　0.5,　1,　and　2　A　g(-1),　respectively)　for　sodium　ion　batteries.　The　good　electrochemical　sodium　storage　performance　of　the　Sn4P3@NPC　composite　anodes　can　be　ascribed　to　the　synergistic　effect　between　porous　N-doped　carbon　and　high-active　Sn4P3　nanoparticles.