The　WC-Co　cemented　carbides　with　ultracoarse　and　ultrafine　grain　structures　were　tested　by　the　bonded　interface　technique　to　investigate　the　deformation　behaviour　of　WC.　The　electron　backscattering　diffraction　assisted　trace　analysis　and　transmission　electron　microscopy　were　combined　to　examine　the　microstructural　details　in　the　deformation　region.　It　was　found　that　the　plastic　characteristics　of　the　ultracoarse　WC　originate　from　both　the　prismatic　(e.g.　{10　(1)　over　bar0}　＜(1)　over　bar2　(1)　over　bar3　＞)　and　pyramidal　(e.g.　{0　(1)　over　bar　11}　＜　0　(1)　over　bar　10　＞)　slip　systems.　The　deformation　mechanisms　of　the　ultracoarse　and　ultrafine　cemented　carbides　were　compared.　It　was　proposed　that　different　from　the　ultrafine　cemented　carbides　in　which　the　plastic　deformation　is　mainly　attributed　to　the　metal　binder,　the　dislocations　and　stacking　faults　in　WC　make　significant　contributions　to　the　plastic　deformation　hence　the　fracture　toughness　of　the　ultracoarse　cemented　carbide.　(c)　2018　Elsevier　Ltd.　All　rights　reserved.