Ni-based alloy coating with the additions of MoS2 solid lubricants was successfully prepared on 20CrMo steel substrate by laser cladding. The coating was free of cracks and pores, and had metallurgical bonding with the substrate. The effects of solid lubricants on the microstructure and mechanical properties of composite coating were studied. The morphology of laser cladding layer was observed by optical microscope and scanning electron microscope (SEM) ,composition analysis was applied by EDS. Elevated temperature frictional behaviors of MoS2/Ni composites were investigated by MMG-10 wear machine. The results show that addition of MoS 2 can decrease the friction coefficient remarkably at the temperature of 20-800 °C and with the increase of MoS2 from 0 to 8% , the friction coefficient of coating decreases gradually,besides,the friction coefficient of coating which has the same MoS2content decreases at first and then increases with the increase of temperature,and that with 8wt% MoS2canreach the minimum 0.2 at 600 °C.