In　this　study,　a　novel　loose-NF　membrane　was　fabricated　by　coating　the　polyethyleneimine　(PEI)　layer　on　a　hydrolyzed　polyacrylonitrile　(HPAN)　ultrafiltration　membrane,　followed　by　phosphorylation　with　inositol　hexaphosphate　(IP6)　and　cross-linking　process.　The　cross-linked　network　was　constructed　by　the　coordinative　cross-linking　of　Fe　(III)　ion　and　phos-(PEI),　and　the　electrostatic　attraction　of　PEI　and　IP6.　At　the　optimized　fabricating　conditions,　the　loose-NF　membrane　exhibited　both　high　rejection　to　dyes　and　transmission　to　different　salts.　The　rejections　of　0.1　g/L　methyl　blue　(MB),　congo　red　(GR),　acid　fuchsin　(AF)　and　crystal　violet　(CV)　aqueous　solutions　respectively　were　99.92%,　99.53%,　98.99%　and　92.86%,　and　the　corresponding　fluxes　were　11.54,　10.96,　11.40　and　11.76　Lm(-2)　h(-1)　at　operating　pressure　of　0.2　MPa.　Meanwhile,　the　membrane　exhibited　low　rejections　to　different　salt　solutions　with　the　order　of　MgCl2　(30.51%)　＞　MgSO4　(20.57%)　＞　NaCl　(7.46%)　＞　Na2SO4　(5.89%)　and　fluxes　around　19　Lm(-2)　h(-1)　at　0.2　MPa.　Moreover,　the　prepared　membrane　possessed　high　stability　for　dealing　with　biologically　treated　textile　effluent　(100　h).