Misfit　dislocation　structures　are　investigated　in　a　nickel-based　single　crystal　superalloy　subjected　to　38.8　h　creep　at　1100　degrees　C　and　130　MPa　using　conventional　and　high　resolution　transmission　electron　microscopy　(HRTEM).　The　misfit　dislocation　was　identified　as　an　uncommon　one　with　Burgers　vector　b　=　a/2[(2)　over　bar　11],　which　can　be　described　as　inserting　(or　extracting)　one　(1　(1)　over　bar1)　half　plane　and　one　(11　(1)　over　bar)　half　plane.　This　dislocation　was　decomposed　into　two　partial　dislocations　b(1)　and　b(2),　with　b(1)　=　a/2[(1)　over　bar　01]　and　b(2)　=　a/2[(2)　over　bar　11].　Partial　dislocations　b(1)　and　b(2)　were　arranged　in　a　＂V＂　shape,　connected　by　the　antiphase　boundary　(APB),　which　could　hinder　the　dislocation　motion　to　achieve　the　effect　of　dislocation　enhancement.　(c)　2018　Elsevier　B.V.　All　rights　reserved.