A　new　lead-free　binary　solid　solution　(1-x)(Bi1/2Na1/2)TiO3-x　-Ba(Zn1/3Nb2/3)O-3[(1-x)　BNT-xBZN]　was　fabricated　by　a　two-step　solid　oxide　reaction　route.　The　microstructure,　electrical　properties　and　fieldinduced　strain　as　a　function　of　the　BZN　content　were　investigated　systematically.　The　results　showed　that,　as　BZN　added,　the　solid　solution　undergone　a　transformation　from　rhombohedral　to　pseudocubic　phases,　and　a　morphotropic　phase　boundary　occurred　around　x　=　0.05.　Meanwhile,　the　ergodic　PNRs　emerged　at　x　=　0.05　and　the　completely　ergodic　state　occurred　for　x　＞=　0.06.　Especially,　for　the　x　=　0.055　sample,　a　large　field-induced　strain　of　0.40%　under　an　external　electric　field　of　8　kV/mm　was　obtained　due　to　the　coexistence　of　nonergodic　and　ergodic　states.　(C)　2017　Elsevier　B.V.　All　rights　reserved.